Rebonded Magnesite-Chrome Brick for Electric Arc
Product Description
Rebonded Magnesite-Chrome Brick for Electric Arc
It is a kind of alkaline refractory product with perriclase as main phase magnesia alumina spinel clinker as basic material .The product has such characteristics as good temperature vibration, good strength and volume stability in high temperature.
Direct-bonded magnesia chrome bricks
Brand MgO (%)≥ SiO2 (%)≤ Cr2O3 (%)≥ Apparent porosity A.P(%)≤ Bulk density B.D(g/cm3)≥ Compressive strength at room temperature C.C.S MPa≥ 0.2Mpa Load softening start temperature RUL(℃) ≥ ZHMGe-12 65 2.5 12 18 3.05 40 1700 ZHMGe-14 62 2.5 14 18 3.05 40 1700 ZHMGe-16 60 2.5 16 18 3.1 40 1700
Semi-rebonded magnesia chrome bricks
Brand | MgO (%)≥ | SiO2 (%)≤ | Cr2O3 (%)≥ | Apparent porosity A.P(%)≤ | Bulk density B.D(g/cm3)≥ | Compressive strength at room temperature C.C.S MPa≥ | 0.2Mpa Load softening start temperature RUL(℃) ≥ |
BDMGe-18 | 55 | 2 | 18 | 16 | 3.15 | 45 | 1700 |
BDMGe-20 | 50 | 2 | 20 | 16 | 3.15 | 45 | 1700 |
Fused rebonded magnesia chrome bricks
Brand | MgO (%)≥ | SiO2 (%)≤ | Cr2O3 (%)≥ | Apparent porosity A.P(%)≤ | Bulk density B.D(g/cm3)≥ | Compressive strength at room temperature C.C.S MPa≥ | 0.2Mpa Load softening start temperature RUL(℃) ≥ |
DMGe-18 | 58 | 1.5 | 18 | 15 | 3.2 | 50 | 1700 |
DMGe-20 | 55 | 1.5 | 20 | 15 | 3.2 | 50 | 1700 |
DMGe-24 | 50 | 1.5 | 24 | 15 | 3.25 | 50 | 1700 |
Magnesite Chrome Refractory Bricks are produced from sintered magnesia and chrome ore by sintering at high temperature. Magnesite Chrome Refractory Bricks have high bulk density and advantages of stronger thermal resistance. Magnesite Chrome Refractory Bricks are widely used for;
cement rotary kilns
glass kiln regenerators
permanent lining of steel furnaces
permanent lining of refining ladles